01 Universal Thermoplastic Reinforcement Formula
Formula 1 (High performance glass fiber reinforced PP):
Homopolymer PP (F401) 54%
GF 30%
Coupling agent K-550 0.5%
PP-g-MAH 5%
POE-g-MAH 10%
Lubricant 0.5%
Processing conditions:
(1) Extrusion granulation temperature: 180-230 ° C; Screw speed 320r/min
(2) Injection molding temperature: 190~210 ° C
Formula 2 (GF/LCD composite reinforced PP):
PP 70%
TLCP 50%
GF 3%
Note:
GF length<4mm, treated with bismaleimide, TLCP thermally induced solution polymer, co ester of p-hydroxybenzoic acid (PHB) and PET (60/40).
Related performance:
Tensile strength 51.3MPa; The tensile modulus is 1.59GPa.
Formula 3 (Glass Fiber Reinforced PP):
PP 51%
LDPE 5%
Glass fiber (5mm) 40%
Maleic anhydride PP 4%
Related performance:
Tensile strength/MPa 97
Bending modulus of elasticity/GPa 7.44
Impact strength/(J/m2) 138.8
Formula 4 (Glass Fiber Reinforced PVC):
PVC 10
Thiol based dibutylene 3
Surface coated with fiberglass 30
HSt 0.5
Processing conditions:
After thoroughly mixing the components in this formula, they are extruded into a finished product.
Formula 5 (Glass Fiber Reinforced PVC):
PP 100
Fatty acid 1
Dibasic lead sulfate 3
CaSt 0.3
Fatty acid ester 2
Glass fiber (2-4mm) 30
02 Engineering plastic reinforcement formula
Formula 1 (Flame retardant glass fiber reinforced PA6 impeller):
Short fiberglass reinforced PA6 (including 30% fiberglass) 91%
Melamine 4%
Sb2O3 5%
Formula 2 (anti-static glass fiber reinforced PA6 impeller):
Short fiberglass reinforced PA6 (including 30% fiberglass) 94%
Short carbon fiber 4.5%
Conductive carbon black 0.5%
Formula 3 (Anti static Glass Fiber Reinforced PA6 Impeller):
PA6 40-55
Flame retardants 15-25
Toughening agents 5-8
Antistatic agents 5-8
Fiberglass 25-30
03 Thermosetting plastic reinforcement formula
Formula 1 (reinforced PF for chemical anti-corrosion pipelines):
Epoxy modified PF 100
Wet asbestos 8
Blue Stone Cotton 152
Formula 2 (epoxy fiberglass):
Epoxy resin (E-44) 100
Ethylenediamine (65%) 6-8
Dibutyl phthalate 10-15
Filler 30-40
Triphenyl phosphite 5
Acetone (or anhydrous ethanol) 10-15
Formula 3 (epoxy furan fiberglass):
Epoxy resin (E-44) 30
Furan resin 70
Triphenyl phosphite vinegar 10
Phthalate dibutyl acetate 10
Fillers (rock powder, graphite powder, quartz powder) 30
Ethylenediamine 6-8
Acetone (or ethanol) 10-15
Processing conditions:
Heat curing, generally 80~90 ℃ x 4 hours
Formula 4 (771 unsaturated polyester glass):
771 unsaturated polyester 100
Cobalt naphthenate or cobalt naphthenate 3-4 in winter and 0.5-1 in summer
Peroxycyclohexanone 1
04 Other plastic reinforcement formulas
Formula 1 (GF enhanced RJM-PU):
Liquefied MDF 63 modified with carbodiimide
PAPI 10
Blocked polyether glycol 100
Dibutylene dilaurate 0.25
Butanediol 20
Fiberglass 30
Formula 2 (fiberglass reinforced PVDC shaped component assembly):
PVDC 25
VC, VDC 25
Fiberglass 50
Colorant 12